Stain Less Steel Wt20 TIG Tungsten Electrode in Welding Rods
September 27 11:05:24, 2022
Model NO.: weld
Slag Characteristic: Acidic
Stainless Steel Welding Rod Type: Chromium Stainless Steel
Function: Surfacing Electrode, Low Hydrogen Type Electrode, Hardfacing Electrode, High Efficient Iron Powder Electrode, Gravity Electrode, Moisture-Proof Electrode
Welding Power: AC
Welding Current: 40-230A
Certification: ISO9001
Business Type: Factory Directly Exporting
Color: Customizable
Trademark: N/M
Transport Package: Carton
Specification: customizable
Origin: China
HS Code: 83111000
Product Description Â
E 6013 welding rod is carbon steel welding rod covered with a high titania potassium type coating. Both AC and DC can be applied, and it is applicable for all-position welding, including vertical-down welding. It shows a very good welding performance with small spatters, easy restrike arc and very good wled shape.
APPLICATIONS: E 6013 welding rod suitable for welding low carbon steel structures and low carbon galvanized plate especially applicable for vertical-down welding and intermittent welding Â
Chemical Composition of Deposited Metal (%)
The normal sizes: 2.5*300mm, 3.2*350mm, 2.5*350mm, 5.0*450mm, 4.0*400mm, 5.0*400mm Â
Chemical Composition
C
Mn
Si
S
P
Guarantee Value
≤0.12
0.3-0.6
≤0.35
≤0.035
≤0.040
Mechanical Properties of Deposited Metal (%) Â
Test Item
Rm(Mpa)
Rel(Mpa)
A(%)
KV2(J)
KV2(J)
Guarantee Value
≥420
≥330
≥17
-(normal temperature)
-(0ºC)
Gegeral Result
460-540
≥340
18-26
50-80
≥47
X-ray Radiographic Inspection: Grade II Size and Recommended Welding Current (AC or DC)Â Â
Size (mm)
2.0 X 300
2.5 X 300
3.2 X 350
Current (A)
40-70
60-90
80-130
Notice: Normally the welding electrode does not need to be re-baked in case it is affected with damp seriously re-bake it at 150ºC for 30-60 minutes before use.
Â
Advantage Â
1. Stable arc, less splash 2. Shaped good appearance 3. Easy for removal of slag layer 4. Easy for striking arc and restriking arc. 5. Operable with low amperages on sheet metal 6. Slag control acc